| 中厚板表面微裂纹成因分析 |
| |
| 引用本文： | 王大宝,刘东夫. 中厚板表面微裂纹成因分析[J]. 炼钢, 2000, 16(2): 15-18 |
| |
| 作者姓名： | 王大宝 刘东夫 |
| |
| 作者单位： | 武汉钢铁集团公司 |
| |
| 摘 要： | 简要介绍了武钢三炼钢厂生产的连铸坯轧制中厚板钢板表面产生微裂纹的情况 ,并对微裂纹的成因进行了调查和分析 ,根据攻关试验的结果 ,采取了相应的措施 ,基本消除了钢板表面的微裂纹
|
| 关 键 词： | 连铸坯 中厚板 表面微裂纹 |
| 修稿时间： | 1999-10-26 |
Analysis in Formation of Fine Surface Cracks on Plates |
| |
| Wang Dabao,Liu Dongfu. Analysis in Formation of Fine Surface Cracks on Plates[J]. Steelmaking, 2000, 16(2): 15-18 |
| |
| Authors: | Wang Dabao Liu Dongfu |
| |
| Abstract: | This paper briefly introduces fine cracks occurring on plate surface rolled with continuous cast slabs produced in No.3 Steelmaking Plant of WISCO. After investigating and analyzing the causes of the formation of fine cracks, the corresponding measures have taken according to the experimental results so as to roughly eliminate fine cracks on plate surface. |
| |
| Keywords: | concast slab plate fine surface crack |