Abstract: | Crack propagation in ultra-high-strength steels and their welded joints under dynamic loading . Reported are results of investigation into the propagation of cracks in the base metal and weld metal of an ultra-high-strength steel. The material used in the investigations was a Ni? Co? Mo? alloy maraging steel with a yield point of 170 kp/mm2. The steel was arc welded and TIG welded. The joints exhibited a drop of static strength in the range of 5 to 8 percent related to the base metal. Under zero-to-tension stress cycles the fatigue strength corresponded that of other high-strength steels, under tension-compression stress cycles the steel exhibited a higher fatigue strength. It was possible to show striations with the aid of scanning microscopy. Comparing the track propagation calculated in the microscopic range with the results obtained from the crack growth curves produced approximate agreement. |