Carbon Permeability of Nickel and Ni–Cu Alloys
Authors:Jianqiang Zhang  Maryam Safarzadeh  David J Young
Affiliation:1. School of Materials Science and Engineering, University of New South Wales, Sydney, NSW, 2052, Australia
Abstract:A Ni–20Cr alloy and variants containing 5, 10 and 20Cu (all in wt.%) were carburised in H2-5% CH4 at 1,000 °C. All alloys formed internal carburisation zones containing Cr3C2 and Cr7C3. The Ni–20Cr alloy also developed a surface deposit of graphite, but the copper-bearing alloys did not. Measured parabolic rate constants for intragranular carburisation were used to calculate carbon permeabilities from Wagner’s diffusion analysis. The value obtained for Ni–20Cr was in good agreement with the product of independently measured carbon solubility and diffusion coefficient values for nickel. Permeabilities found for copper-bearing alloys were similar, showing that the presence of copper had little effect on carbon diffusion in nickel. This finding is used in analysing the mechanism by which nickel undergoes metal dusting.
Keywords:
本文献已被 SpringerLink 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号