Corrosion Behavior of Alumina Ceramics in Caustic Alkaline Solutions at High Temperatures

The corrosion rate and changes in the microstructure and fracture strength of alumina ceramics (93.0% Al₂O₃ and 99.5% Al₂O₃) were studied in 0.1 m to 25 m NaOH solutions at 150°C to 200°C, where m = mol/(kg of H₂O). The attack of the caustic alkaline solution started at the grain boundaries. Consequently, the corrosion resistance increased with decreasing SiO₂ content in Al₂O₃ ceramics, and the corrosion resistance of 99.5% pure Al₂O₃ was similar to that of Si₃N₄ ceramics. Since large pits are formed by corrosion, the surface area increased first and the apparent corrosion rate increased with time in the initial stage of the corrosion. The corrosion rate of Al₂O₃ increased linearly with increasing NaOH concentration, and the activation energy was 102 kJ/mol. The fracture strength of corroded Al₂O₃ decreased monotonically as the degree of dissolution of alumina increased.