Effect of LiBH4 on hydrogen storage property of MgH2

The effect of lithium borohydride (LiBH₄) on the hydriding/dehydriding kinetics and thermodynamics of magnesium hydride (MgH₂) was investigated. It was found that LiBH₄ played both positive and negative effects on the hydrogen sorption of MgH₂. With 10 mol.% LiBH₄ content, MgH₂–10 mol.% LiBH₄ had superior hydrogen absorption/desorption properties, which could absorb 6.8 wt.% H within 1300 s at 200 °C under 3 MPa H₂ and completed desorption within 740 s at 350 °C. However, with the increasing amount of LiBH₄, the hydrogenation/dehydrogenation kinetics deteriorated, and the starting desorption temperature increased and the hysteresis of the pressure-composition isotherm (PCI) became larger. Our results showed that the positive effect of LiBH₄ was mainly attributed to the more uniform powder mixture with smaller particle size, while the negative effect of LiBH₄ might be caused by the H–H exchange between LiBH₄ and MgH₂.