Pre-martensitic phenomena in Ti40.7Hf9.5Ni44.8Cu5 shape memory alloy |
| |
Affiliation: | 1. Department of Mechanical Science and Engineering, University of Illinois at Urbana–Champaign, 1206 W. Green St., Urbana, IL 61801, USA;2. Siberian Physical–Technical Institute at Tomsk State University, Tomsk 634050, Russia |
| |
Abstract: | Pre-martensitic phenomena such as abnormal resistivity growth, diffusion scattering, “tweed” contrast and internal friction peak were observed in Ti40.7Hf9.5Ni44.8Cu5 alloy prior to the forward martensitic transformation on cooling. It was shown that all the observed phenomena were due to the formation of quasi-static strain nanodomains in the B2 phase prior to the forward martensitic transformation. This led to accumulation of the elastic energy before the phase transition and resulted in the variation in thermodynamic balance for the forward martensitic transformation and, as a result, influenced the parameters of the phase transition. The appearance of elastic energy prior to the forward transformation caused a decrease in the forward and reverse martensitic transformations' start temperatures, a widening of the temperature range of the reverse transformation and an increase in the hysteresis of the transformation. |
| |
Keywords: | Shape-memory alloys Martensitic transformation Point defects Differential scanning calorimetry Diffraction/scattering (electron, neutron and X-ray) |
本文献已被 ScienceDirect 等数据库收录! |
|