Cation Ordering Transformations in the Ba(Zn1/3Nb2/3)O3-La(Zn2/3Nb1/3)O3 System

Single-phase perovskites were formed in the (1−_x)Ba(Zn_1/3Nb_2/3)O₃-( _x )La(Zn_2/3Nb_1/3)O₃ system for compositions with 0.0≤ x ≤0.6. Although the stability of the trigonal "1:2" ordered structure of the Ba(Zn_1/3Nb_2/3)O₃ end member is very limited (0.0≤ x ≤0.05), low levels of lanthanum induce a transformation to a cubic, "1:1" ordered structure that has a broad range of homogeneity (0.05≤ x ≤0.6). Samples with x > 0.6 were comprised of La₃NbO₇, ZnO, and a perovskite with x = 0.6. The cubic 1:1 phases were fully ordered and no evidence was found for a compositionally segregated microstructure. These observations could not be reconciled in terms of a "space-charge" model; rather, they supported a charge-balanced, "random-site" structure for the 1:1 cation-ordered Ba(β_1/2'β_1/2")O₃ phases.