Effect of heat treatment on microstructure and properties of GH4169 laser welded joint
GUO Zhanying,LIU Yongjun,FANG Haipeng. Effect of heat treatment on microstructure and properties of GH4169 laser welded joint[J]. Materials Science and Technology, 2020, 28(2): 60-66
Authors:GUO Zhanying  LIU Yongjun  FANG Haipeng
Affiliation:School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu 610031, China
Abstract:Laser butt welding was carried out on 2 mm-thick plates of GH4169 superalloy.Welded joint samples were cut by Wire Electrical Discharge Machining(WEDM).Half of the welded joint samples were standard heat treated and the others were not,and the hardness and tensile properties of the welded joints were evaluated.Results show that the tensile strength of the welded joints after heat treatment was 1372 MPa,the elongation was 14%,and the average weld hardness was 473 HV.Compared with non-heat treated welded joints,the tensile strength of the heat treated welded joints increased by 52%,elongation reduced by 71%,and hardness increased by 69%.OM,SEM,EDS,and XRD analyses show that heat treatment refined the laser welded joint grain,improved the dendrite morphology,eliminated the residual stress,and especially precipitatedδphase,γ′phase andγ″phase,which improved the hardness and strength of the welded joints.
Keywords:GH4169   laser welding   microstructure  heat treatment   mechanical properties