Microhardness studies on nonlinear optical L-alanine single crystals

Vickers and Knoop microhardness tests were carried out on grown L-alanine single crystals by slow evaporation technique over a load range of 10–50 g on selected broad (2 0 3) plane. Vickers (H _v ) and Knoop (H _k ) microhardness for the above loads were found to be in the range of 60–71 kg/mm² and 35–47 kg/mm², respectively. Vickers microhardness number (H _v ) and Knoop microhardness number (H _k ) were found to increase with increasing load. Meyer’s index number (n) calculated from H _v shows that the material belongs to the soft material category. Using Wooster’s empirical relation, the elastic stiffness constant (c ₁₁) was calculated from Vickers hardness values. Young’s modulus was calculated using Knoop hardness values. Hardness anisotropy has been observed in accordance with the orientation of the crystal.