| 预焙阳极生坯裂纹原因及措施 |
| |
| 引用本文： | 李锋,王建红,王卉丽. 预焙阳极生坯裂纹原因及措施[J]. 炭素技术, 2003, 0(1): 35-37 |
| |
| 作者姓名： | 李锋 王建红 王卉丽 |
| |
| 作者单位： | 石家庄铝业有限责任公司碳素公司,河北,井陉,050300 |
| |
| 摘 要： | 对铝电解用预焙阳极生坯生产中经常出现的几种裂纹进行了原因分析，并提出了一些具体措施，以期对生坯生产有所指导。
|
| 关 键 词： | 预焙阳极 生坯 裂纹原因 钻电解 炭素制品 |
| 文章编号： | 1001-3741(2003)01-0035-03 |
| 修稿时间： | 2002-08-26 |
CAUSES OF CRACKS IN GREEN ANODE CARBON BLOCKS FOR ALUMINIUM ELECTROLYSIS AND PRACTICAL MEASURES FOR AVODING THESE CRACKS |
| |
| LI Feng,WANG Jian-hong,WANG Hui-li. CAUSES OF CRACKS IN GREEN ANODE CARBON BLOCKS FOR ALUMINIUM ELECTROLYSIS AND PRACTICAL MEASURES FOR AVODING THESE CRACKS[J]. Carbon Techniques, 2003, 0(1): 35-37 |
| |
| Authors: | LI Feng WANG Jian-hong WANG Hui-li |
| |
| Abstract: | The causes of several types of cracks in green anode carbon blocks for aluminium electrolysis are analyzed. Several measures to tackle these cracks in production are presented, which are believed to be useful and effective in production of green anode carbon blocks. |
| |
| Keywords: | Prebaked anode green anode carbon block crack |