Effect of properties and crystallization behavior of BaO–ZnO–B2O3–SiO2 glass on the electrical conductivity of Cu paste

The extensive application of multilayer ceramic capacitors provides an attractive development for terminal electrode pastes. However, the growing requirement for advanced glass materials used in terminal electrode pastes is substantiated. Therefore, to advance the development of electrode pastes, better development and deeper exploration of glass powder are required. Here, a series of BaO–ZnO–B₂O₃–SiO₂ (BZBS) glasses were prepared by melt-quenching technique, which are used to investigate the effect of the introduction of BaO on structure and properties of the ZnO–B₂O₃–SiO₂ (ZBS) glass. With the introduction of BaO, the relative amount of BO₄] was much less, which made the glass network structure loosen, decreased the glass transition temperature (T_g) and increased the coefficient of thermal expansion of the glass. The decreasing contact angle was observed on the surface of a barium titanate (BaTiO₃) substrate. When the BaO content was around 3–7 mol%, the stability of ZBS glass frit could be strengthened by inhibiting the precipitation of Zn₂SiO₄ crystal. In addition, to further characterize the effect of glass on terminal electrode paste, BZBS glass powder was adopted to prepare copper electrode paste, which was printed on the BaTiO₃ substrate and subsequently fired at 800°C for 10 min. With the related copper paste containing ZBS glass doped with 7 mol% BaO, the optimum value of acid resistance and sheet resistance (1.99 mΩ) were exhibited, at which the coated copper paste formed a dense conducting layer.