Influence of annealing on properties and structure of alumina

Alumina bodies were prepared from pure alumina powder (98.9% Al₂O₃ consisting of 82% > 53m). The powder was compacted by hot-pressing at 1200° C, Compacted bodies were annealed at 1300, 1400 and 1500° C. Annealing continued at each maximum temperature for 25, 50 and 100 h. Strong bodies were obtained with maximum bulk density of 2.32 g cm^–3 and minimum apparent porosity of 30.21%. The change in sintering parameters with annealing was correlated with developed structure.