| 304不锈钢连铸坯表面裂纹原因分析及改善措施 |
| |
| 引用本文： | 戴秀东.304不锈钢连铸坯表面裂纹原因分析及改善措施[J].山西冶金,2010,33(4):26-28. |
| |
| 作者姓名： | 戴秀东 |
| |
| 作者单位： | 山西太钢不锈钢股份有限公司,山西,太原,030003 |
| |
| 摘 要： | 通过对304不锈钢连铸坯表面裂纹产生的原因如钢种特性、连铸过热度、冷却强度以及拉速等进行分析,并结合现场生产的实际情况,提出了消除304不锈钢连铸坯表面裂纹缺陷的措施,取得了良好的实际应用效果。
|
| 关 键 词： | 304不锈钢 连铸坯 表面裂纹 |
Cause Analysis and Countermeasures of 304 Stainless Steel Continuous Cast Slab Face Cracks |
| |
| DAI Xiudong.Cause Analysis and Countermeasures of 304 Stainless Steel Continuous Cast Slab Face Cracks[J].Shanxi Metallurgy,2010,33(4):26-28. |
| |
| Authors: | DAI Xiudong |
| |
| Affiliation: | DAI Xiudong(Shanxi Taigang Stainless Steel Co.,Ltd.,Taiyuan 030003,China) |
| |
| Abstract: | By cause analysis of 304 stainless steel continuous cast slab face cracks such as steel characteristic,molten steel superheat,mold cooling strength and draw speed,based on the plant production instance,discovered countermeasures of eliminating 304 stainless steel continuous cast slab face cracks,and acquired obvious effect. |
| |
| Keywords: | 304 stainless steel continuous cast slab face cracks |