Polyfurfuryl alcohol derived activated carbons for high power electrical double layer capacitors |
| |
Authors: | V Ruiz |
| |
Affiliation: | CSIRO Division of Energy Technology, Box 312, Clayton South, Vic. 3169, Australia |
| |
Abstract: | Polyfurfuryl alcohol (PFA) derived activated carbons were prepared by the acid catalysed polymerization of furfuryl alcohol, followed by potassium hydroxide activation. Activated carbons with apparent BET surface areas ranging from 1070 to 2600 m2 g−1, and corresponding average micropore sizes between 0.6 and 1.6 nm were obtained. The porosity of these carbons can be carefully controlled during activation and their performance as electrode materials in electric double layer capacitors (EDLCs) in a non-aqueous electrolyte (1 M Et4NBF4/ACN) is investigated.Carbon materials with a low average pore size (<∼0.6 nm) exhibited electrolyte accessibility issues and an associated decrease in capacitance at high charging rates. PFA carbons with larger average pore sizes exhibited greatly improved performance, with specific electrode capacitances of 150 F g−1 at an operating voltage window of 0-2.5 V; which corresponds to 32 Wh kg−1 and 38 kW kg−1 on an active material basis. These carbons also displayed an outstanding performance at high current densities delivering up to 100 F g−1 at current densities as high as 250 A g−1. The exceptionally high capacitance and power of this electrode material is attributed to its good electronic conductivity and a highly effective combination of micro- and fine mesoporosity. |
| |
Keywords: | Polyfurfuryl alcohol Supercapacitors Cyclic voltammetry Porous carbon Molecular sieving |
本文献已被 ScienceDirect 等数据库收录! |
|