Synthesis of LiNi1/3Co1/3Mn1/3O2 cathode materials by using a supercritical water method in a batch reactor

LiNi_1/3Co_1/3Mn_1/3O₂ and LiCoO₂ cathode materials were synthesized by using a supercritical water (SCW) method with a metal salt solution in a batch reactor. Stoichiometric LiNi_1/3Co_1/3Mn_1/3O₂ was successfully synthesized in a 10-min reaction without calcination, while overlithiated LiCoO₂ (Li_1.15CoO₂) was synthesized using the batch SCW method. The physical properties and electrochemical performances of LiNi_1/3Co_1/3Mn_1/3O₂ were compared to those of Li_1.15CoO₂ by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), and charge/discharge cycling tests. The XRD pattern of LiNi_1/3Co_1/3Mn_1/3O₂ was found to be similar to that of Li_1.15CoO₂, showing clear splitting of the (0 0 6)/(1 0 2) and (1 0 8)/(1 1 0) peak pairs as particular characteristics of the layered structure. In addition, both cathode powders showed good crystallinity and phase purity, even though a short reaction time without calcination was applied to the SCW method. The initial specific discharge capacities of the Li_1.15CoO₂ and LiNi_1/3Co_1/3Mn_1/3O₂ powders at a current density of 0.24 mA/cm² in 2.5-4.5 V were 149 and 180 mAh/g, and their irreversible capacity loss was 20 and 17 mAh/g, respectively. The discharge capacities of the Li_1.15CoO₂ and LiNi_1/3Co_1/3Mn_1/3O₂ powders decreased with cycling and remained at 108 and 154 mAh/g after 30 cycles, which are 79% and 89% of the initial capacities. Compared to the overlithiated LiCoO₂ cathode powders, the LiNi_1/3Co_1/3Mn_1/3O₂ cathode powders synthesized by SCW method had better electrochemical performances.