Optimum synthesis of Li2Fe1−xMnxSiO4/C cathode for lithium ion batteries

Li₂Fe_1−xMn_xSi0₄/C cathode materials were synthesized by mechanical activation-solid-state reaction. The effects of Mn-doping content, roasting temperature, soaking time and Li/Si molar ratio on the physical properties and electrochemical performance of the Li₂Fe_1−xMn_xSi0₄/C composites were investigated. The materials were characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM), charge-discharge tests and AC impedance measurements. SEM images suggest that the morphology of the Li₂Fe_1−xMn_xSi0₄/C composite is sensitive to the reaction temperature. Samples synthesized at different temperatures have different extent of agglomeration. Being charged-discharged at C/32 between 1.5 and 4.8 V, the Li₂Fe_0.9Mn_0.1Si0₄/C synthesized at the optimum conditions shows good electrochemical performances with an initial discharge capacity of 158.1 mAh g⁻¹ and a capacity retention ratio of 94.3% after 30 cycles. AC impendence investigation shows Li₂Fe_0.9Mn_0.1SiO₄/C have much lower resistance of electrode/electrolyte interface than Li₂FeSiO₄/C.