Effect of TiO2 on high-temperature thermoelectric properties of ZnO

The as-sintered Zn_1−xTi_xO (0.01 ≤ x ≤ 0.05) samples contained a solid solution of Zn_1−xTi_xO with a wurtzite structure and a small amount of the cubic spinel Zn₂TiO₄. The amount of Zn₂TiO₄ increased with an increase in TiO₂ content. The density and grain size increased with the small TiO₂ content (≤0.01), and then they decreased gradually by further increasing the TiO₂ content. The addition of TiO₂ to ZnO led to a significant increase in the electrical conductivity and a decrease in the absolute value of the Seebeck coefficient, resulting in an increase in the power factor. The highest value of power factor (7.6 × 10⁻⁴ W m⁻¹ K⁻²) was attained for Zn_0.98Ti_0.02O at 1073 K. It is demonstrated that the TiO₂ addition is fairly effective for enhancing thermoelectric properties.