采用60 t BOF-LF-VD-220 mm× 220 mm CC-轧制工艺流程成功试制履带链轨节用Φ50 mm 35MnB圆钢(0.35％C,0.28％ Si,1.25％ Mn,0.0020％B,0.030％ Ti).通过优化BOF出钢[C]≥0.10％和[P]≤0.015％,精炼渣碱度(R)3.87 ～ 5.73...

Production Practice of 35MnB Round Steel for Track Link

Φ50 mm 35MnB steel bar ( 0. 35% C ,0. 28% Si, 1. 25% Mn,0. 002 0% B,0. 030% Ti ) for track link is produced by 60 t BOF-LF-VD-220 mm x 220 mm CC-rolling process. By optimizing the technical parameters of BOF tapping ,including [ C ] ≥ 0. 10% and [P]≤ 0.015%, basicity of refining slag R =3.87 ~ 5. 73 , soft blowing time for、15min,20 ~32 ℃ superheat of tundish liquid, rolling heating temperature at 1 100 ~ 1 200 °C ,starting rolling at 1 000 ~ 1 070 ℃ , and finishing rolling at，850 °C , of the finished 35MnB steel bar, the [O]≤15 x 10^-6, [ N ] ≤50 x 10^-6 , rating of macrostructure and nonmetal inclusion ≤1.5 , hardenability JI. 5 HRC number：53 ~ 55, J19 HRC number:34 ~ 38, TS 960 ~ 1 050 MPa, YS 765 ~ 810 MPa, IE 80 ~ 100 J, to meet the requirement of each performance index.