Quantitative Analysis of Microstructural Homogeneity and Capacitance Correlations in Palladium/Yttria-Stabilized Zirconia Composites |
|
| Authors: | Mark G. H. M. Hendriks Marjan J. G. W. Heijman Werner E. van Zyl Johan E. ten Elshof Henk Verweij |
| Affiliation: | Laboratory for Inorganic Materials Science, Faculty of Chemical Technology, and MESA Research Institute, University of Twente, 7500 AE Enschede, The Netherlands;Department of Materials Science and Engineering, The Ohio State University, Columbus, Ohio 43210-1178 |
| Abstract: | Voronoi tessellation was applied to quantify the microstructural homogeneity of palladium particles in random Pd/cubic yttria-stabilized zirconia (YSZ) composites with the Pd concentration ranging from 0 to 30 vol%. Room-temperature impedance measurements were used to determine the capacitance of the composites. A fourfold enhancement in capacity near the percolation threshold of Pd was obtained. The percolation threshold was estimated at ∼30 vol% Pd using the normalized percolation theory (NPT). Data obtained from Voronoi diagrams resulted in a quantitative measure for the homogeneity of the dual-phase composite. The homogeneity was found to decrease with increasing Pd concentration in the composites. Near the theoretical value of the percolation threshold, the Pd phase appeared to be distributed too inhomogeneously for preparing insulating composites. No large increase in capacity as predicted by NPT could therefore be experimentally verified. |
| Keywords: | microstructure palladium/palladium compounds zirconia: yttria stabilized |