Superior energy-storage properties in (Pb,La)(Zr,Sn,Ti)O3 antiferroelectric ceramics with appropriate La content

Antiferroelectric (AFE) ceramics based on Pb(Zr,Sn,Ti)O₃ (PZST) have shown great potential for applications in pulsed power capacitors because of their fast charge-discharge rates (on the order of nanoseconds). However, to date, it has been proven very difficult to simultaneously obtain large recoverable energy densities W_re and high energy efficiencies η in one type of ceramic, which limits the range of applications of these materials. Addressing this problem requires the development of ceramic materials that simultaneously offer a large ferroelectric-antiferroelectric (FE-AFE) phase-switching electric field E_A, high electric breakdown strength E_b, and narrow polarization-electric field (P-E) hysteresis loops. In this work, via doping of La³⁺ into (Pb_1-1.5xLa_x)(Zr_0.5Sn_0.43Ti_0.07)O₃ AFE ceramics, large E_A and E_b due to respectively enhanced AFE phase stability and reduced electric conductivity, and slimmer hysteresis loops resulting from the appearance of the relaxor AFE state, are successfully obtained, and thus leading to great improvement of the W_re and η. The most superior energy storage properties are obtained in the 3?mol% La³⁺-doped (Pb_1-1.5xLa_x)(Zr_0.5Sn_0.43Ti_0.07)O₃ AFE ceramic, which simultaneously exhibits at room temperature a large W_re of 4.2?J/cm³ and a high η of 78%, being respectively 2.9 and 1.56 times those of (Pb_1-1.5xLa_x)(Zr_0.5Sn_0.43Ti_0.07)O₃ AFE ceramics with x?=?0 (W_re?=?1.45?J/cm³, η?=?50%) and also being superior to many previously published results. Besides, both W_re and η change very little in the temperature range of 25–125?°C. The large W_re, high η, and their good temperature stability make the Pb_0.955La_0.03(Zr_0.5Sn_0.43Ti_0.07)O₃ AFE ceramic attractive for preparing high pulsed power capacitors useable in various conditions.