Effect of preparation conditions on mechanical,dielectric and microwave absorption properties of SiC fiber/mullite matrix composite

Silicon carbide fiber-reinforced mullite matrix (SiC_f/Mu) composites were fabricated via an infiltration and sintering method. Effects of sintering parameters on microstructure, mechanical, dielectric and microwave absorption properties of SiC_f/Mu composites have been investigated. The flexural strength is significantly improved with increasing sintering temperature, and the highest flexural strength of 213?MPa is obtained in vacuum at 1000?°C for 2?h. The performances of composites with different holding time are further studied at 1000?°C. The flexural strengths of composites sintered at 1000?°C for 2 and 4?h reach 213 and 219?MPa, respectively. The failure displacement of the composite sintered at 1000?°C for 4?h reaches 0.39?mm. The excellent microwave absorption properties are achieved for the composite sintered at 1000?°C for 2?h. The minimum reflection loss (RL) reaches ?38?dB with a thickness of 2.9?mm?at 12?GHz and the effective absorbing bandwidth (RL?≤??10?dB) with a thickness of 3.4?mm covers the whole X?band, which indicate that SiC_f/Mu composite is a good candidate for microwave absorbing materials. These results provide valuable solutions to obtaining structural-functional materials for microwave absorption applications in civil and military areas.