Study on photoelectrochemical solar cells of nanocrystalline Cd0.7Zn0.3Se -water soluble conjugated polymer |
| |
Authors: | SD Chavhan RS Mane S Senthilarasu J Lee |
| |
Affiliation: | a School of Semiconductor and Chemical Engineering, Nano materials Process Research Center, Chonbuk National University, Duckjin-dong 664-14, Jeonju, 561-756, Republic of Korea b Department of Chemistry, Hanyang University, Sungdong-Ku, Haengdang-dong 17, Seoul, 133-791, Republic of Korea c Jeonju Center, Korea Basic Science Institute, Jeonju 561-756, Republic of Korea |
| |
Abstract: | Cadmium zinc selenide (Cd0.7Zn0.3Se) nanocrystalline thin films were chemically synthesized onto indium tin oxide (ITO)-coated glass substrate at relatively low temperature (<90 °C). The as-deposited films were annealed in air at 200, 300, and 400 °C for 60 min. The structure and surface morphology of the films were studied by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The water-soluble conjugated polymer, poly(2-ethynyl-N-carboxy-propyl-pyridinium bromide) (LM3), with quaternary pyridinium salts was layered by dipping the as-deposited and annealed Cd0.7Zn0.3Se films in the aqueous polymer solution. This hybrid photoanode system was subjected to photoelectrochemical (PEC) study under a light illumination intensity of 80 mW/cm2. |
| |
Keywords: | Cd0 7Zn0 3Se Pyridinium salt Thin films Photoelectrochemical solar cell |
本文献已被 ScienceDirect 等数据库收录! |
|