One-step microwave synthesis and characterization of carbon-modified nanocrystalline LiFePO4

The precursors of LiFePO₄ were prepared by a sol-gel method using lithium acetate dihydrate, ferrous sulfate, phosphoric acid, citric acid and polyethylene glycol as raw materials, and then the carbon-modified nanocrystalline LiFePO₄ (LiFePO₄/C) cathode material was synthesized by a one-step microwave method with the domestic microwave oven. The effect of microwave time and carbon content on the performance of the resulting LiFePO₄/C material was investigated. Structural characterization by X-ray diffraction and scanning electron microscopy proved that the olivine phase LiFePO₄ was synthesized and the grain size of the samples was several hundred nanometers. Under the optimal conditions of microwave time and carbon content, the charge-discharge performance indicated that the nanosized LiFePO₄/C had a high electrochemical capacity at 0.2 C (152 mAh g⁻¹) and improved capacity retention; the exchange current density was 1.6977 mA cm⁻². Furthermore, the rate capability was improved effectively after LiFePO₄ was modified with carbon, with 59 mAh g⁻¹ being obtained at 20 C.