Microstructure and mechanical properties of Al2O3-Cr2O3-ZrO2 composites

Al₂O₃ is a popular ceramic and has been used widely in many applications and studied in many aspects. On the other hand, zirconia-toughened alumina (ZTA) is a desirable material for engineering ceramics because of its high hardness, high wear resistance and high toughness. In the present research, Al₂O₃-Cr₂O₃-ZrO₂ composites were produced by hot-pressing in order to harden the Al₂O₃ matrix in ZTA. Its microstructure and mechanical properties were studied by SEM, ESCA, XRD, Vickers hardness and bending strength test. It was found that addition of ZrO₂ inhibited the grain growth of Al₂O₃-Cr₂O₃ and the grain growth of ZrO₂ proceeded with increasing amounts of ZrO₂ in the Al₂O₃-Cr₂O₃-Zr₂ composite. The formation of solid solution Al₂O₃-Cr₂O₃ was also confirmed by XRD, and monoclinic ZrO₂ increased on addition of Cr₂O₃. Maximum hardness was at Al₂O₃-10wt% Cr₂O₃ with 10 vol% ZrO₂ and a stress-induced transformation was confirmed on the fracture surface of the specimen after the bending test.