Heteroepitaxy of HgCdTe (211)B on Ge substrates by molecular beam epitaxy for infrared detectors

Epitaxial growth of (211)B CdTe/HgCdTe has been achieved on two inch germanium (Ge) by molecular beam epitaxy (MBE). Germanium was chosen as an alternative substrate to circumvent the weaknesses of CdZnTe wafers. The ease of surface preparation makes Ge an attractive candidate among many other alternative substrates. Best MBE CdTe growth results were obtained on (211) Ge surfaces which were exposed to arsenic and zinc fluxes prior to the MBE growth. This surface preparation enabled CdTe growth with B-face crystallographic polarity necessary for the HgCdTe growth. This process was reproducible, and produced a smooth and mirror-like surface morphology. The best value of the {422} x-ray double diffraction full width at half maximum measured from the HgCdTe layer was 68 arc-s. We present the 486 point maps of FWHM statistical values obtained from CdTe/Ge and HgCdTe/CdTe/Ge. High resolution microscopy electron transmission and secondary ion mass spectroscopy characterization results are also presented in this paper. High-performance middle wavelength infrared HgCdTe 32-element photodiode linear arrays, using the standard LETI/LIR planar n-on-p ion implanted technology, were fabricated on CdTe/Ge substrates. At 78K, photodiodes exhibited very high R₀A figure of merit higher than 10⁶ Ωcm⁻² for a cutoff wavelength of 4.8 μm. Excess low frequency noise was not observed below 150K.