Low temperature solid-state synthesis routine and mechanism for Li3V2(PO4)3 using LiF as lithium precursor

Monoclinic lithium vanadium phosphate, Li₃V₂(PO₄)₃, has been successfully synthesized using LiF as lithium source. The one-step reaction with stoichiometric composition and relative lower sintering temperature (700 °C) has been used in our experimental processes. The solid-state reaction mechanism using LiF as lithium precursor has been studied by X-ray diffraction and Fourier transform infrared spectra. The Rietveld refinement results show that in our product sintered at 700 °C no impurity phases of VPO₄, Li₅V(PO₄)₂F₂, or LiVPO₄F can be detected. The solid-state reaction using Li₂CO₃ as Li-precursor has also been carried out for comparison. X-ray diffraction patterns indicate that impurities as Li₃PO₄ can be found in the product using Li₂CO₃ as Li-precursor unless the sintering temperatures are higher than 850 °C. An abrupt particle growth (about 2 μm) has also been observed by scanning electron microscope for the samples sintered at higher temperatures, which can result in a poor cycle performance. The product obtained using LiF as Li-precursor with the uniform flake-like particles and smaller particle size (about 300 nm) exhibits the better performance. At the 50th cycle, the reversible specific capacities for Li₃V₂(PO₄)₃ measured between 3 and 4.8 V at 1C rate are found to approach 147.1 mAh/g (93.8% of initial capacity). The specific capacity of 123.6 mAh/g can even be hold between 3 and 4.8 V at 5C rate.