| 弹簧钢带冷冲压起皮原因分析 |
| |
| 引用本文： | 曹国洲.弹簧钢带冷冲压起皮原因分析[J].理化检验(物理分册),2003,39(7):366-367,381. |
| |
| 作者姓名： | 曹国洲 |
| |
| 作者单位： | 宁波出入境检验检疫局,宁波,315012 |
| |
| 摘 要： | 某公司对进口的冷轧弹簧钢带(50CrVA)进行冷冲压加工时，钢带表面沿轧制方向出现了起皮、剥离等现象。对该钢带进行化学成分、力学性能和金相组织等检验。结果表明，钢带的原材料中已存在冶金缺陷以及各类夹杂物，同时还有严重的带状偏析组织，这些都是钢带表面存在微裂纹的原因。当该钢带在冷加工时，促使裂纹沿轧制方向扩展，最终导致钢带起皮和剥离。
|
| 关 键 词： | 弹簧钢带 冷冲压 起皮 剥离 冶金缺陷 化学成分分析 力学性能测试 金相检验 |
| 文章编号： | 1001-4012(2003)07-0366-02 |
SURFACE PEELING ANALYSIS OF COLD-PRESSED SPRING STEEL STRIP |
| |
| CAO Guo-zhou.SURFACE PEELING ANALYSIS OF COLD-PRESSED SPRING STEEL STRIP[J].Physical Testing and Chemical Analysis Part A:Physical Testing,2003,39(7):366-367,381. |
| |
| Authors: | CAO Guo-zhou |
| |
| Abstract: | The peeling was happened on the surface of spring steel strip (50CrVA) imported, after cold-pressing. By means of chemical composition analysis, mechanical properties testing and microstructure examination, the peeling reason was due to the microcracking. Comparision the structure of defects with matrix, we have gotten the conclusion that the microcracking was caused by segregated band and medium of second phase. |
| |
| Keywords: | Spring steel strip Peeling Microcrack |