Crack path selection in the fracture of fresh and degraded epoxy adhesive joints |
| |
Authors: | A. Ameli S. Azari M. Papini J.K. Spelt |
| |
Affiliation: | aDepartment of Mechanical and Industrial Engineering, University of Toronto, 5 King’s College Road, Toronto, Ontario, Canada M5S 3G8;bDepartment of Mechanical and Industrial Engineering, Ryerson University, 350 Victoria Street, Toronto, Ontario, Canada M5B 2K3 |
| |
Abstract: | The crack paths and fracture surfaces of aluminum–epoxy adhesive joints were characterized as a function of the mode ratio of loading and the amount of degradation that had been generated using the open-faced aging technique. A finite element (FE) model was used to predict the extent of the plastic zone at different crack growth lengths and mode ratios, and a close relationship was found between the evolution of the plastic zone and the previously reported R-curve behavior of these joints. The micro-topography of the fracture surfaces, measured using an optical profilometer, showed that a ductile–brittle transition occurred in the fracture behavior of the joints as degradation progressed. The crack path in the (brittle) degraded specimens was normal to the first principal stress, but could not be predicted in the undegraded joints because of its highly three-dimensional nature. Based on the distribution of the maximum von Mises stress in the adhesive layer ahead of the crack tip, a crack growth mechanism was proposed that is consistent with these experimental observations and explains the highly three-dimensional nature of fracture in these highly constrained joints. |
| |
Keywords: | Adhesive joint Rubber-modified epoxy Finite element Fracture surface Crack path Plastic zone Mixed-mode Degradation |
本文献已被 ScienceDirect 等数据库收录! |
|