| Abstract: | Aromatic polyesters were prepared and used to decrease the brittleness of the bismaleimide resin composed of 4,4′-bismaleimidediphenyl methane (BMI) and o,o′-diallyl bisphenol A (DBA) (Matrimid 5292 resin). The aromatic polyesters included poly(propylene phthalate) (PPP), poly(2,2-dimethylpropylene phthalate) (PDPP), poly(butylene phthalate) (PBP) and poly(butylene phthalate-co-butylene terephthalate) (50mol% terephthalate unit) (PBPT). The polyesters were effective modifiers for decreasing the brittleness of the bismaleimide resin. For example, inclusion of 20wt% PPP (MW 18700) led to 50% increase in the fracture toughness (KIC) with retention of flexural properties and a slight loss of the glass transition temperature, compared with the mechanical and thermal properties of the unmodified cured bismaleimide resin. Micro-structures of the modified resins were examined by scanning electron microscopy and dynamic viscoelastic analysis. The thermal stability of the modified resins was slightly lower than that of the unmodified resin as determined by thermogravimetric analysis. The toughening mechanism is discussed in terms of the morphological and dynamic viscoelastic behaviour of the modified bismaleimide resin system. © 1998 SCI. |