Phase relations and microwave dielectric properties of vanadium modified Ba5Nb4O15 ceramics

Microwave dielectric ceramics of Ba₅Nb_4−xV_xO₁₅ (x = 0-1) were prepared by a solid-state reaction method. Vanadium substitution can markedly lower the sintering temperature of Ba₅Nb₄O₁₅ from 1450 to 1100 °C. The X-ray powder diffraction analysis reveals the multiphase nature of this system. A hexagonal-to-orthorhombic phase transition was also observed for the BaNb₂O₆ secondary phase. The microwave dielectric properties, such as τ_f, ε_r and Q × f value, decreased with increasing vanadium content for samples sintered at 1100 °C. There was an apparent increase in τ_f and Q × f value for samples (x ≥ 0.5) sintered at 1200 °C due to the hexagonal-to-orthorhombic phase transition of the BaNb₂O₆ phase. These results suggested that the microwave dielectric properties of multiphase ceramics strongly depended on the phase compositions and the phase transitions.