Visible photoluminescence from Er-doped TiO2 nanofibres by electrospinning

Er³⁺-doped TiO₂ nanofibres were fabricated with electrospinning method followed by annealing in air at 420, 600, 800 and 1000 °C, respectively. The obtained nanofibres are relatively straight and have an average diameter of ∼ 75 nm. X-ray diffraction measurements showed that the crystal structure transforms from anatase to rutile phase with the increase of annealing temperature. Visible photoluminescence peaking at 528.1, 566.6 and 669.3 nm is detected which is ascribed to ²H_11/2 → ⁴I_15/2, ⁴S_3/2 → ⁴I_15/2 and ⁴F_9/2 → ⁴I_15/2 transitions of Er³⁺ ions and the PL intensities increase with the increase of annealing temperature. Meanwhile at high annealing temperatures, near-infrared photoluminescence peaking at 815 nm due to the defect states associated with Ti³⁺ ions is also found. The strong green photoluminescence of Er³⁺ ions may have potential applications in one-dimensional luminescent nanodevices.