Nanocluster evolution in Ge ion implanted Ta2O5 layers

Ion implantation-induced nanoclusters were synthesized in reactive sputtered Ta₂O₅ films by Ge⁺ implantation and subsequent annealing. The effects of ion fluence and post-implantation thermal treatment on the kinetics of the nanoclustering were investigated. Ge⁺ ions with energy of 40 keV and fluences of 5 × 10¹⁵, 1 × 10¹⁶ and 5 × 10¹⁶ cm^− 2 were implanted in the Ta₂O₅ layers at room temperature. The samples were thermally treated by rapid thermal annealing in vacuum at 700 °C and 1000 °C for 30, 60 and 180 s. Structural studies of all samples were done by Cross-sectional Transmission Electron Microscopy in diffraction and phase contrast mode. Under optimized conditions (high implantation fluence, subsequent annealing) nanoclusters are formed around the projected ion range of the implanted Ge⁺ ions. The structure of the implanted Ta₂O₅ matrix changes from amorphous to orthorhombic when the annealing was performed at 1000 °C. Although the Ta₂O₅ matrix crystallizes, no evidence is obtained for crystallization of the embedded nanoclusters even after annealing at 1000 °C.