Effects of complex substitution of La and Nd for Bi on the microwave dielectric properties of BiNbO4 ceramics

La₂O₃ and Nd₂O₃ were used to substitute Bi₂O₃ and the effects of complex substitution on the sintering behavior and the microwave dielectric properties of BiNbO₄ ceramics were studied. With 0.5 wt.% CuO-V₂O₅ mixtures addition, all of the Bi_1−x(La_0.38Nd_0.62)_xNbO₄ ceramics could be densified below 920 °C. The triclinic phases are identified in Bi_1−x(La_0.38Nd_0.62)_xNbO₄ ceramics with x=0.01 sintered at 820 °C and the triclinic intensities increase with increasing the x value and sintering temperature. The saturated bulk density slightly decreases from 7.17 to 7.13 g/cm³ and the ε_r value from 44.24 to 42.76 with increasing x from 0 to 0.07 for Bi_1−x(La_0.38Nd_0.62)_xNbO₄ ceramics. The saturated Q×f value is between 10,300 and 12,400 GHz depending on the x value. The τ_f values of dense Bi_1−x(La_0.38Nd_0.62)_xNbO₄ ceramics decrease from 28.32 to 12.79 ppm/°C with x varying from 0 to 0.01 and remain almost unchanged with further increasing x.