Effects of Ca and Zr substitution upon structure and properties of Ba5LaTi3Ta7O30 low-loss dielectric ceramics

Effects of Ca and Zr substitution upon the dielectric properties of Ba₅LaTi₃Ta₇O₃₀ ceramics were investigated together with the structural characterization. All the samples of Ba₅La(Zr_xTi_1−x)₃Ta₇O₃₀ formed a filled tungsten-bronze structures, whereas the solid solution limit was determined as x=0.25 in (Ca_xBa_1−x)₅LaTi₃Ta₇O₃₀. Beyond this limit secondary phase of CaTa₂O₆ was detected and it would become the major phase for the Ca-rich compositions. The temperature coefficient of dielectric constant was improved with increasing Zr content while the dielectric constant decreased and the low dielectric loss varied little (in the order of 10⁻⁴). In the case of (Ca_xBa_1−x)₅LaTi₃Ta₇O₃₀, small temperature coefficient of dielectric constant could be obtained with increasing Ca content while the dielectric constant decreased significantly, and a small amount substitution of Ca for Ba induced decrease in dielectric loss.