High‐Selectivity Y2O3‐Doped SiO2 Nanocomposite Membranes for Gas Separation in Steam at High Temperatures

Asymmetric structures were fabricated by depositing Y₂O₃‐doped SiO₂ (Si/Y) membranes onto γ‐Al₂O₃ supported by tubular α‐Al₂O₃. The thickness of the Y₂O₃‐doped SiO₂ deposits was approximately 100 nm. The deposits/membranes have micropores with a pore diameter ~ <0.40–0.55 nm. Pore size distribution measurements were conducted directly on the membranes before and after hydrothermal treatment with a nano‐permporometer. The gas permeance properties of the membranes were measured in the temperature range 100°C–500°C. The Y‐doped SiO₂ membrane (Si/Y = 3/1) was found to exhibit asymptotically stable permeances of 2.39 × 10^?7 mol/m²/s/Pa for He and 6.19 × 10^?10 mol/m²/s/Pa for CO₂, with a high selectivity of 386 (He/CO₂) at 500°C for 20 h in the presence of steam. The Y‐doped silica membranes exhibit very high gas permeances for molecules with smaller kinetic diameters. The apparent activation energies of the H₂ permeance at 400°C were 24.2 ± 0.2 and 21.3 ± 0.7 kJ/mol for SiO₂ and Si/Y, respectively.