Structure and Mechanical Properties of Ni-P-Nano Al2O3 Composite Coatings Synthesized by Electroless Plating
Authors:ZHOU Guang-hong  DING Hong-yan  ZHOU Fei  ZHANG Yue
Affiliation:[1]Department of Mechanical Engineering, Huaiyin Institute of Technology, Huai'an 223001, Jiangsu, China; [2]Institute of Bio-inspired Structure and Surface Engineering, Academy of Frontier Science, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, Jiangsu, China
Abstract:Ni-P-nano Al2O3 composite coatings were deposited by electroless plating, and their microstructures were observed by SEM (scanning electron microscope). The microhardness and the wear resistance of the Ni-P-nano Al2O3 composite coatings were measured using microhardness tester and block-on-ring tribometer, respectively, and the comparison with those of Ni-P coatings or Ni-P-micro Al2O3 coating was given. The influences of aging temperature on their hardness and wear resistance were analyzed. The results showed that the nano Al2O3 particles were distributed uniformly in the Ni-P-Al2O3 coatings. Among three kinds of Ni-P based coatings, the hardness and wear resistance of Ni-P-nano Al2O3 coatings were largest, and the maximum values could be obtained at 400 ℃. This indicated that the precipitation of nano Al2O3 particles would improve the hardness and wear resistance of the Ni-P coatings.
Keywords:composite coating  nano Al2O3  aging treatment  mechanical property
本文献已被 维普 万方数据 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号