Abstract: | Behaviour of stainless cast alloys under combined mechanical and corrosive attack In media with 3000 mg B/1 (as boric acid, H3BO3) and varying chloride contents down to 1 mg Cl?/1 13%-Cr-steels show pitting. Under constant load cracks appear simultaneously. As can be expected, 17%-Cr-steels are more resistant and duplex ferritic austenitic steels exhibit no corrosion cracking in 3% NaCl-solution even after 10 000 hrs. Generally, corrosion resistance improves with increasing contents of ferrite forming elements. Corrosion cracks are interpreted in termes of anodic stress corrosion cracking. Notch impact bending tests with hydrogen charged specimens show that deformability is reduced. |