| Abstract: | Graft copolymerization of SBS in the form of sodium ionomer with acrylamide in emulsion using benzoyl peroxide as initiator and sodium ionomer of maleated SBS as a self‐emulsifier, which can form a stable cyclohexane/water emulsion with AM without using any other emulsifier, was carried out. Factors affecting the graft copolymerization were studied. The grafting % can reach about 15%. Emulsifying properties of sodium ionomer of maleated SBS and the graft copolymer, as well as the compatibilizing effect of the graft copolymer in blending polyvinyl chloride (PVC) with SBS, were studied. The sodium ionomer of maleated SBS, the graft copolymers, and the blends were characterized with IR and DSC. The results showed that water absorbency and emulsifying volume increase obviously after graft copolymerization with AM. 0.2 g of the graft copolymer containing 14 wt % PAM grafts can emulsify a mixture of 30 mL toluene and 70 mL water completely. The graft copolymer can be used as an effective compatibilizer in the blending of PVC and SBS, more effective than the sodium ionomer of maleated SBS. Only 2 wt % of the copolymer based on the blend used in blending is enough to raise the tensile strength three times. The blends with weigh ratios of PVC/SBS at 3/7–4/6 in the presence of the graft copolymer behave as thermoplastic elastomers with a tensile strength of 14 MPa, an ultimate elongation of 750%, and a permanent set of 17%. Glass transition temperatures of the blend shifted inward in the presence of the graft copolymer. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 97: 1248–1253, 2005 |