Microwave dielectric properties of Ca[(Li1/3Nb2/3)1−x Tix]O3−δ ceramics with glass

The effect of the addition of glass on the densification, low temperature sintering, and microwave dielectric properties of the Ca(Li_1/3Nb_2/3)_1−x Ti_x]O_3−δ(CLNT) was investigated. Addition of glass (B₂O₃-ZnO-SiO₂-PbO system) improved the densification and reduced the sintering temperature from 1150^∘C to 900^∘C of Ca(Li_1/3Nb_2/3)_1−x -Ti_x]O_3−δ microwave dielectric ceramics. As increasing glass contents from 10 wt% to 15 wt%, the dielectric constants (ε_r) and bulk density were increased. The quality factor (Q⋅f₀), however, was decreased slightly. The temperature coefficients of the resonant frequency (τ_f) shifted positive value as increasing glass contents over Ti content is 0.2 mol. The dielectric properties of Ca(Li_1/3Nb_2/3)_0.75Ti_0.25]O_3−δ with 10 wt% glass sintered at 900^∘C for 3 h were ε_r = 40 Q·f₀ = 11500 GHz, τ_f = 8, ppm/°C. The relationship between the microstructure and dielectric properties of ceramics was studied by X-ray diffraction (XRD), and scanning electron microscope (SEM).