| 新型固体润滑剂──氟化石墨的制备与性能的研究 |
| |
| 引用本文： | 夏金童,陈小华,征茂平,熊友谊,周声劢,陈宗璋. 新型固体润滑剂──氟化石墨的制备与性能的研究[J]. 无机材料学报, 1998, 13(3): 435-439 |
| |
| 作者姓名： | 夏金童 陈小华 征茂平 熊友谊 周声劢 陈宗璋 |
| |
| 作者单位： | 湖南大学化学化工学院; 长沙410082 |
| |
| 基金项目： | 国家教委博士点基金!9453201，湖南省科委资助!9515025 |
| |
| 摘 要： | 通过电解熔盐KF·ZHF制取氟气，再将氟气与石墨在500℃时进行反应，从而制备了氟化石墨新材料．其密度值为2．53g／cm3、电阻率为3.1×103Ω·cm，颜色为灰白色，在波数1219、1350cm－1附近有F-C共价键红外光谱吸收峰．对氟化石墨、石墨、二硫化钼进行摩擦因数测试，结果表明：氟化石墨摩擦因数最小．还讨论了氟化石墨的一些特殊性能和工艺条件．
|
| 关 键 词： | 氟气制备 氟化石墨 摩擦性能 |
| 收稿时间： | 1997-11-24 |
| 修稿时间： | 1998-01-09 |
A New Type of the Solid Lubricant Material-Preparation and Properties of Graphite Fluoride |
| |
| XIA Jin-Tong,CHEN Xiao-Hua,ZHENG Mao-Ping,XIONG You-Yi,ZHOU Sheng-Mai,CHEN Zong-Zhang. A New Type of the Solid Lubricant Material-Preparation and Properties of Graphite Fluoride[J]. Journal of Inorganic Materials, 1998, 13(3): 435-439 |
| |
| Authors: | XIA Jin-Tong CHEN Xiao-Hua ZHENG Mao-Ping XIONG You-Yi ZHOU Sheng-Mai CHEN Zong-Zhang |
| |
| Affiliation: | Institute of Chemistry and Chemical Engineering; Hunan University Changsha 410082 China |
| |
| Abstract: | Fluorine gas was produced with the electrolysis of the molten salt KF·2HF, then graphite fluoride was prepared through the reaction between graphite powder and fluorine gas at 500℃. The real density of the graphite fluoride was 2.53g/cm^3, its electrical resistivity 3.1×103Ω·cm and its colour greyish white. The graphite fluoride synthesized had a absorption peak of infrared reflection spectra on F--C covalent bond at approximation wavenumber 1219cm-1 and 1350cm-1. By testing friction factor for the graphite fluoride, graphite powder and molybdenum disulphide, the experimental results showed that the friction factor of the graphite fluoride was the smollest. Furthermore, technological conditions and special properties of the graphite fluoride were dissussed. |
| |
| Keywords: | preparation of fluorine gas graphite fluoride friction properties |