| Cr基过渡层对CrWN涂层摩擦学性能的影响 |
| |
| 引用本文： | 张梦慧, 黄新放, 韩旭, 张人升, 乔洲, 李庆宁, 燕峰, 冯永军, 解志文. Cr基过渡层对CrWN涂层摩擦学性能的影响[J]. 真空科学与技术学报, 2021, 41(12): 1178-1183. DOI: 10.13922/j.cnki.cjvst.202103004 |
| |
| 作者姓名： | 张梦慧 黄新放 韩旭 张人升 乔洲 李庆宁 燕峰 冯永军 解志文 |
| |
| 作者单位： | 1.辽宁科技大学 机械工程与自动化学院 辽宁 114051 |
| |
| 基金项目： | 国家自然科学基金项目(51771087; 52171076); 辽宁科技大学创新训练项目(S202010146003); 辽宁科技大学教学改革项目(XJGBZ202014) |
| |
| 摘 要： | 本文探究了 Cr过渡层及Cr-CrN过渡层对CrWN涂层耐磨性能的影响,制备具有良好的减磨耐磨性能的CrWN涂层.采用等离子增强磁控溅射工艺,在碳化钨基体表面制备CrWN涂层,Cr-CrWN涂层、Cr-CrN-CrWN涂层.通过扫描电子显微镜,X射线光电子能谱仪,X射线衍射仪,纳米压痕仪,洛氏硬度计和摩擦磨损实验机对涂...
|
| 关 键 词： | CrWN涂层 梯度过渡层 摩擦学性能 等离子增强磁控溅射 |
| 收稿时间： | 2021-03-06 |
Effects of Cr-Based Interlayers on Tribological Properties of CrWN Coatings |
| |
| ZHANG Menghui, HUANG Xinfang, HAN Xu, ZHANG Rensheng, QIAO Zhou, LI Qingning, YAN Feng, FENG Yongjun, JIE Zhiwen. Effects of Cr-Based Interlayers on Tribological Properties of CrWN Coatings[J]. CHINESE JOURNAL VACUUM SCIENCE AND TECHNOLOGY, 2021, 41(12): 1178-1183. DOI: 10.13922/j.cnki.cjvst.202103004 |
| |
| Authors: | ZHANG Menghui HUANG Xinfang HAN Xu ZHANG Rensheng QIAO Zhou LI Qingning YAN Feng FENG Yongjun JIE Zhiwen |
| |
| Affiliation: | 1.School of Mechanical Engineering and Automation, University of Science and Technology Liaoning, Liaoning 114051, China |
| |
| Abstract: | This work investigates the effects of Cr and Cr-CrN transition layer on the wear resistance of CrWN coating and prepares CrWN coating with excellent wear resistance. CrWN coating,Cr-CrWN coating and Cr-CrNCrWN coating are deposited on tungsten carbide substrates using plasma enhanced magnetron sputtering. The surface morphology,mechanical and tribological properties of the coating are analyzed by scanning electron microscopy(SEM),X-ray photoelectron spectroscopy(XPS),X-ray diffraction(XRD),Nano-indentation,Rockwell hardness tester and friction tester. The coatings are composed of face-centered cubic CrN and W2 N phases. Cr-CrNCrWN coating has the highest adhesion strength of coating substrate,which is HF1 grade. The hardness of CrWN coating is 21.5 GPa. The introduction of Cr transition layer and Cr-CrN transition layer did not significantly affect the hardness and elastic modulus of the coating. However,Cr transition layer and Cr-CrN transition layer can reduce the friction coefficient and improve the wear resistance of the coating. The friction coefficient of the coatings is 0.656 and 0.703,and the wear rate is 1.366×10-6 mm3/(N·m)and 1.247×10-6 mm3/(N·m) respectively in stable friction stage. Moreover,no furrows and cracks on the surface and no obvious spalling of the coating are found after wear. Therefore,the introduction of Cr transition layer and Cr-CrN transition layer can improve the adhesion of the coating/substrate and the wear resistance of the coating. |
| |
| Keywords: | Cr WN coating Gradient transition layer Tribological properties Plasma enhanced magnetron sputtering |
|