Microstructure and Microwave Dielectric Properties of (1−x)Ca(Mg1/3Ta2/3)O3/xCaTiO3 Ceramics

Dense (1? x )Ca(Mg_1/3Ta_2/3)O₃/ x CaTiO₃ ceramics (0.1≤ x ≤0.9) were prepared by a solid-state reaction process. The crystal structures and microstructures were characterized by X-ray diffraction, scanning electron microscopy, and transmission electron microscopy. Single-phase solid solutions were obtained in the entire composition range. Long-range 1:2 ordering of B-site cations and oxygen octahedra tilting lead to the monoclinic symmetry with space group P 2₁/ c for x =0.1. For x above 0.1, the long-range ordering was destroyed and the crystal structure became the orthorhombic with space group Pbnm . The microwave dielectric properties showed a strong dependence on the composition and microstructure. The dielectric constant and temperature coefficient of resonant frequency increased nonlinearly as the CaTiO₃ content increased while the Qf values decreased approximately linearly. Good combination of microwave dielectric properties was obtained at x =0.45, where ?_r=45.1, Qf =34 800 GHz, and τ_f=17.4 ppm/°C.