400℃时Mg-Zn-Ce系金属间化合物及相平衡(英文)

利用平衡合金法研究Mg-Zn-Ce系富镁角在400℃时各金属间化合物的相成分、相结构及相关系。研究表明,Mg-Zn-Ce系富镁角丰在一个线性化合物T相,其化学式为(Mg1-xZnx)11Ce。T相中Zn的含量为9.6%～43.6%(摩尔分数)。T相的晶体结构为C底心正交晶格,其晶格参数随着Zn含量的增加而略有减小,分别为a=0.96～1.029nm,b=1.115～1.204nm,c=0.940～1.015nm。Mg12Ce能够固溶7.8%的Zn元素,其化学式为(Mg1-xZnx)12Ce。确定了400℃时Mg-Zn-Ce系相图富镁角的相关系。

Intermetallics and phase relations of Mg-Zn-Ce alloys at 400 ℃

The crystal structures,compositions and phase relations of the intermetallics of Mg-Zn-Ce system in the Mg-rich corner at 400 ℃ were identified through equilibrium alloy method.For Mg-Zn-Ce system,there is a linear ternary compound(T phase),whose chemical formula is(Mg1-xZnx)11Ce.The range of Zn content in T phase is from 9.6% to 43.6%(molar fraction).The crystal structure of T phase is C-centered orthorhombic lattice with lattice parameters of a=0.96-1.029 nm,b=1.115-1.204 nm,c=0.940-1.015 nm.And the lattice parameters of T phase are decreasing a little with increasing Zn content.According to the results of composition and crystal structure,the maximal solubility of Zn in Mg12Ce is about 7.8%(molar fraction),and the chemical formula of the solid solution can be identified as(Mg1-xZnx)12Ce.The isothermal section of Mg-Zn-Ce system in Mg-rich corner at 400 ℃ was constructed.