| Zn-Al系列高速电弧喷涂层电化学防腐性能研究 | |
| 引用本文： | 刘燕,朱子新,陈永雄,徐滨士,栗卓新.Zn-Al系列高速电弧喷涂层电化学防腐性能研究[J].中国表面工程,2004,17(5):23-25,30. |
| 作者姓名： | 刘燕 朱子新 陈永雄 徐滨士 栗卓新 |
| 作者单位： | 1. 装备再制造国防科技重点实验室,北京,100072;北京工业大学,材料科学与工程学院,北京,100022 2. 装备再制造国防科技重点实验室,北京,100072 3. 北京工业大学,材料科学与工程学院,北京,100022 |
| 基金项目： | 国家自然科学基金重点项目(No.50235030);装备维修科研与改革项目(No.2003ZB06) |
| 摘 要： | 采用粉芯丝材和高速电弧喷涂技术制备高Al含量的Zn-26％Al涂层。通过电化学的方法测试涂层在5％NaCl溶液下的腐蚀行为，并与由实芯丝材纯Zn、纯Al及Zn-15％A1所制备的涂层作比较。结果表明：Zn-26％A1涂层在电解质溶液中表现出更优越的防腐性能。动电位极化测试结果说明zn-Al涂层随着Al含量的增加，其耐蚀性也提高。纯Al涂层的电化学腐蚀行为与其它涂层有明显差异，其腐蚀机理类似于点蚀。 |
| 关 键 词： | 高速电弧喷涂 Zn-Al 电化学腐蚀 动电位极化 |
| 文章编号： | 1007-9289(2004)05-0023-03 |
| 修稿时间： | 2004年9月3日 |
Electrochemical Corrosion Behavior of Arc Sprayed Zn-Al Coatings |
|
| LIU Yan,ZHU Zi-xin,CHEN Yong-xiong,XU Bin-shi,LI Zhuo-xin.Electrochemical Corrosion Behavior of Arc Sprayed Zn-Al Coatings[J].China Surface Engineering,2004,17(5):23-25,30. | |
| Authors: | LIU Yan ZHU Zi-xin CHEN Yong-xiong XU Bin-shi LI Zhuo-xin |
| Affiliation: | LIU Yan 1,2,ZHU Zi-xin,CHEN Yong-xiong1,XU Bin-shi,LI Zhuo-xin2 1 1 |
| Abstract: | Cored wires and high velocity arc spraying technique (HVAS) were applied to produce high Al content Zn-Al alloy coatings on low carbon steel substrate. The electrochemical corrosion behaviors of Zn, Al and Zn-Al coatings were studied with potentiodynamic measurement in 5 %NaCl solution. Compared with pure Zn, Al and Zn-15Al coatings, the Zn-26Al coatings showed a higher corrosion resistance in salt solution. The potentiodynamic polarization tests showed that the corrosion resistance of Zn-Al coatings increased as the Al content was raised. Pure Al coating exhibited different electrochemical behaviors compared with other coatings. The corrosion initiated at the micro-pores of the coating and the corrosion mechanism was very similar to that of the pitting corrosion. |
| Keywords: | high velocity arc spraying Zn-Al electrochemical corrosion potentiodynamic polarization |