| 热变形白品铸铁碳化物的动态对冲击疲劳性能的影响 |
| |
| 引用本文： | 刘建华,邵光杰. 热变形白品铸铁碳化物的动态对冲击疲劳性能的影响[J]. 上海金属, 2001, 23(4): 27-29 |
| |
| 作者姓名： | 刘建华 邵光杰 |
| |
| 作者单位： | 燕山大学秦皇岛市, |
| |
| 摘 要： | 对不同变形量的白口铸铁中碳化物的形态及冲击疲劳性能进行了观察与探讨，结果表明：在0－40％的变形范围内，白口铸铁的变形量越大，碳化物破碎越严重，其冲击疲劳性能越好。
|
| 关 键 词： | 热变形 白口铸铁 碳化物形态 冲击疲劳性能 |
| 修稿时间： | 2000-08-10 |
THE CARBIDE SHAPE OF HOT DEFORMED WHITE CAST IRON AND ITS INFLUENCE ON THE IMPACT FATIGUE PROPERTY |
| |
| Liu Jianhua Shao Guangjie. THE CARBIDE SHAPE OF HOT DEFORMED WHITE CAST IRON AND ITS INFLUENCE ON THE IMPACT FATIGUE PROPERTY[J]. Shanghai Metals, 2001, 23(4): 27-29 |
| |
| Authors: | Liu Jianhua Shao Guangjie |
| |
| Affiliation: | Yanshan University |
| |
| Abstract: | The impact fatigue property and the carbide shape of white cast iron after different hot deformation had been observed and studied.The results indicated that the more the white cast iron deformed,the worse its carbide broken,and the better its impact fatigue property,when deformation ranged from 0 to 40%. [ |
| |
| Keywords: | Hot Deformation White Cast Iron Carbide Impact Fatigue |