采用粉末冶金技术制备铜基复合材料，在制动压力0. 5～1. 2 MPa 范围内，通过定速摩擦试验机研究了干、湿条件下，速度、压力与材料摩擦磨损性能的关系，结果表明:影响摩擦磨损性能的重要因素在于载荷性质和第三体状态。在干摩擦条件下，处于低摩擦速度范围时，摩擦力的静载荷性质使第三体呈疏松状态，这增加了微凸体间的啮合程度而使摩擦系数处于较高值。随第三体致密性增加，其润滑作用增强，微凸体间的机械啮合程度减弱，使材料的摩擦系数和磨损量降低。在高速摩擦时，微凸体间的冲击作用使处于摩擦表层的硬质颗粒容易发生粉碎性破损而弥散分布，这强化了表面强度而使摩擦系数有所增加。摩擦压力对高速摩擦性能影响明显，原因在于高负荷加剧了摩擦面的变形和损伤程度。湿摩擦条件下，水膜的润滑和流动具有降低摩擦系数和增加磨损率的作用主要体现在低速低压条件下。在高摩擦速度和高压力条件下，水分的高温蒸发与离心作用明显，破坏了水膜的存在条件，从而使材料的摩擦磨损性能与干摩擦状态相近。 

Tribological performance of copper matrix composites under dry and wet conditions

Copper matrix composites were prepared through powder metallurgic technique.The relationships between speed and pressure of friction and the friction and wear properties of the materials were studied on a pin-on-disk tester in the pressure range of 0.5~1.2 MPa under dry and wet conditions.The results demonstrate that the major factors affecting the performance are the nature of loading and the state of third bodies.For dry friction,when the speed is low,the friction force is close to static.Such loading all...