Preparation and characterization of high compressive strength foams from sheet glass
Authors:D U Tulyaganov  H R Fernandes  S Agathopoulos  J M F Ferreira
Affiliation:(1) J.M.F. Ferreira Department of Ceramics and Glass Engineering, CICECO, University of Aveiro, 3810-193 Aveiro, Portugal;(2) Scientific Research Institute of Space Engineering, 700128 Tashkent, Uzbekistan
Abstract:High compressive strength glass foams were produced using sheet glass cullet with the aid of 1 wt.% SiC powder, as gassing agent, and the incorporation of small amounts of an alkali earth aluminosilicate glass powder (AD), which is intrinsically prone to be crystallised to anorthite and diopside. The amount of SiC used as well as the mean particle sizes of the powders of both glasses and SiC were lower than those used in earlier studies. The experimental results showed that homogenous microstructures of large pores could be obtained by adding 1 wt.% SiC. The compressive strength of the glass foams was considerably increased when the incorporated AD-glass was higher than 1 wt.%. It is concluded that the presence of the AD glass is beneficial for the produced glass foams because of the formation of a well packed honeycomb structure which features an optimal distribution of pentagonal- and hexagonal-like shaped pores surrounded by dense struts. The crystallization of wollastonite and diopside inside the struts should also have a positive impact on the mechanical behaviour of the produced porous glass foams.
Keywords:Glass waste  Foam  Compressive strength
本文献已被 SpringerLink 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号