Fabrication and Sintering Behavior of Zinc-Doped Biphasic Calcium Phosphate Bioceramics |
| |
| Authors: | I Sopyan Gunawan Q H Shah M Mel |
| |
| Affiliation: | 1. Department of Manufacturing and Materials Engineering, Faculty of Engineering, International Islamic University Malaysia, Kuala Lumpur, Malaysia;2. Department of Mechanical Engineering, Faculty of Engineering, Sriwijaya University, Inderalaya, Indonesia;3. Department of Mechanical Engineering, Faculty of Engineering, International Islamic University Malaysia, Kuala Lumpur, Malaysia;4. Department of Biotechnology, Faculty of Engineering, International Islamic University Malaysia, Kuala Lumpur, Malaysia |
| |
| Abstract: | Dense bioceramics with improved mechanical properties have been prepared using sol–gel derived zinc doped biphasic calcium phosphate (BCP) powders. Zinc concentration was varied in the range of 0,1, 2, 4, 5, 10, and 15 mol%. The compaction of the powders followed by sintering provided the dense ceramics. The effects of zinc concentration doped and sintering temperature on phase stability and mechanical characteristics were examined. The presence of Zn changed the phase of dense BCP, leading to improved mechanical properties. Zn free BCP attained the highest density of only 92.6% after 1400°C sintering, equally achieved by 4 mol% Zn-doped BCP at a lower temperature of 1200°C. It is presumed that the steady increase in the compact density up to 4 mol% zinc incorporation was contributed by progressive consolidation in the BCP structure, but the density dropped again from 5 mol% until 15 mol% due to low density β-tricalcium phosphate phase formation. This study showed that Zn doping was effective in producing high strength dense BCP with 3.40 GPa hardness and 1.43 MPa · m1/2 fracture toughness. |
| |
| Keywords: | Biomaterials Biphasic Calcium phosphate Ceramics Characterization Dopant Mechanical Zinc |
|
|