Precipitation phenomena in and electrical resistivity of high-temperature treated langatate (La3Ta0.5Ga5.5O14)

La(3)Ta(0.5)Ga(5.5)O(14) (LTG) single crystals, which have no phase transition up to the melting point, were heat-treated in air at temperatures from 1000°C to 1450°C for 10 h. LaTaO(4) (LT) and LaGaO(3) (LG), which coexist with LTG in the three-phase region on the Ga-poor side, precipitated on the surface of the crystal for heat treatments above 1300°C because of Ga evaporation during the heat treatment. The Ga-poor state near the surface of the 1450°C heat-treated specimen was confirmed by electron probe micro-analysis measurements. The electrical resistivity of LTG single crystals decreased by heat treatment in the range of 1000°C to 1200°C for 10 h in air, where no precipitation was observed, whereas the resistivity increased with heat treatment over 1400°C for 10 h in air. The electrical resistivity of the Ga-poor surface region was higher than that of the interior.