SAE6150弹簧扁钢热卷耳开裂原因分析 |
| |
引用本文: | 王小忠,范方国,左锦中. SAE6150弹簧扁钢热卷耳开裂原因分析[J]. 中国材料科技与设备, 2011, 0(6): 64-65 |
| |
作者姓名: | 王小忠 范方国 左锦中 |
| |
作者单位: | 江阴兴澄特种钢铁有限公司研究院,江苏江阴214429 |
| |
摘 要: | 采用外观观察、电镜分析、金相检验等方法,对弹簧扁钢在热卷耳过程中发生的开裂原因进行了分析。结果表明热加工过程中温度控制不当,引起扁钢局部过烧进而导致卷耳变形时发生严重开裂现象。
|
关 键 词: | 弹簧扁钢 沿晶开裂 低熔点共晶莱氏体 过烧 |
Analysison the Cracks of SAE6150 Spring Flat Steel During Hot Curling |
| |
Affiliation: | WANG Xiao--zhong, FAN Fang--guo, ZUO Jin--zhong (Jiangyin Xingcheng Special Steel Works Co. , Ltd, Jiangsu, Jiangyin, 214429, China) |
| |
Abstract: | Analysed the reason of the cracks occurrence of spring flat steel during the hot rolling ear process by means of appearance observation, SEM analysis and metallographic examination. The results indicated that the inappropriate temperature control during the hot--working process caused partly overburning of the flat steel and led to the phenomenon of serious cracks when rolling ear deformation occurred. |
| |
Keywords: | Spring flat steel Intergranular crack Low--melting point eutectic ledeburite Overbuming |
本文献已被 维普 等数据库收录! |
|